Preparation, characterization and evaluation of a hybrid polymeric coating with sorbent properties

M. J. Burgos-Tan, Y. Pérez-Padilla, A. Avila-Ortega, J. A. Barrón-Zambrano, A. R. Vilchis-Néstor, C. Carrera-Figueiras, and D. Muñoz-Rodríguez

Cuerpo Académico de Química Fundamental y Aplicada, Facultad de Ingeniería Química, Universidad Autónoma de Yucatán, Mérida, Mexico

 

E-mail: yamile.perez@correo.uady.mx

Abstract: A hybrid polymeric coating (PDMS–CNPrTEOS) with sorbent properties was prepared by the sol–gel method from hydroxyl-terminated poly(dimethylsiloxane) (OH-PDMS), and cyanopropyltriethoxysilane (CNPrTEOS) as an inorganic precursor, using trifluoroacetic acid (TFA) as a catalyst. A coating with the sol–gel solution was prepared on glass plates using the dip-coating method and subsequently characterized. Characterization by FTIR shows that cyano groups are present on the surface coating and contact angle tests show that the coating presents hydrophilic characteristics. The organic–inorganic polymer was stable up to 400 °C with a weight loss of 8 wt % and showed good stability after immersion for 60 min in vortex and 45 min in ultrasonic bath, in various solvents: water, methanol (MeOH), acetone, isooctane, ethyl acetate (AcOEt) and acetonitrile (ACN), and solutions at different pH (1–12) for 48 h (h). The PDMS–CNPrTEOS hybrid polymer was evaluated and was found to have the ability to extract simultaneously furanic compounds in aqueous solution when it is employed as a sorbent for stir bar sorptive extraction (SBSE).

Keywords: Hybrid polymer, Sol–gel, Dip-coating, Furanic compounds, Stir bar sorptive extraction

Full paper is available at www.springerlink.com.

DOI: 10.1007/s11696-016-0113-4

 

Chemical Papers 71 (7) 1205–1215 (2017)

Thursday, March 28, 2024

IMPACT FACTOR 2021
2.146
SCImago Journal Rank 2021
0.365
SEARCH
Advanced
VOLUMES
European Symposium on Analytical Spectrometry ESAS 2022
© 2024 Chemical Papers