Modification of SBA-16 surface by -NH2 group and its application as adsorbent
S. Soleymani, M. Razavi Mehr, M. H. Fekri, and F. Saki
Department of Chemistry, Faculty of Basic Sciences, Ayatollah Borujerdi University, Borujerd, Iran
E-mail: m.h.fekri@abru.ac.ir
Received: 2 February 2023 Accepted: 30 April 2023
Abstract: In this research, silicate nanomesopore SBA-16 was synthesized and functionalized by NH2 group to increase its efficiency, and the purpose of preparing SBA-16-NH2 was to use it to remove the color pollutant methylene blue. The SBA-16-NH2 mesoporous structure was analyzed by FTIR, XRD, SEM and TEM. Then, important parameters for pollutant removal were investigated with the help of experiment design software. The results of the predicted experiments demonstrate that the highest absorption of methylene blue can be seen in pH = 2.04, temperature 50 °C, contact time 10 min, initial adsorbent concentration 10 ppm and amount of adsorbent 0.04 g. In optimal conditions, SBA-16-NH2 adsorbent could remove 98.58% of methylene blue. Also, adsorption isotherms, thermodynamics and kinetics were studied. The results show that the adsorption follows the Langmuir isotherm and is thermodynamically exothermic and spontaneous. The adsorption kinetics is a function of the pseudo-first-order model.
Keywords: Nanomesoporous SBA-16-NH2; Colored pollutants; Methylene blue pigment; Experiment design